Process for reducing CO and SOx emissions from catalytic cracking units

ABSTRACT

Reduction of CO and SO x  emissions from regenerators associated with cyclical fluidized catalytic cracking (FCC) units used to convert hydrocarbon feedstocks into more valuable products is achieved by introducing particles of bastnaesite into the FCC unit. The bastnaesite particles recycle with the catalyst particles successively through a catalytic cracking reaction zone, a stripping zone, and a regeneration zone. The bastnaesite particles react with SO x  produced in the regeneration zone of the FCC unit, thereby lowering the SO x  content of the flue gas discharged therefrom. In the catalytic cracking and stripping zones of the FCC unit, the bastnaesite particles are at least partially reactivated so that upon returning to the regeneration zone yet more SO 2  is removed. The bastnaesite particles also aid in lowering CO emissions from the FCC regenerator by catalyzing the reaction between CO and oxygen to yield CO 2 .

This application is a division of application Ser. No. 109,756, filedJan. 7, 1980 now U.S. Pat. No. 4,311,581.

BACKGROUND OF THE INVENTION

This invention relates to the reduction of CO and SO_(x) components inthe flue gas discharged from regenerators associated with catalyticcracking units. More particularly, this invention relates to injectingparticles of bastnaesite into fluidized catalytic cracking (FCC) unitsto reduce emissions from the catalyst regenerator.

In the petroleum industry, high boiling hydrocarbon feedstocks arecharged to FCC units so that, by contact with a moving bed of catalystparticles, the feedstocks are converted to a more valuable hydrocarbonproduct, such as gasoline, having a lower average molecular weight and alower average boiling point than the feedstock from which it wasderived. The most typical hydrocarbon feedstock treated in FCC unitsconsists of heavy gas oil, but on occasion such feedstocks as light gasoils, reduced crudes, and even whole crudes are subjected to catalyticcracking to yield low boiling hydrocarbon products.

Catalytic cracking in FCC units is usually accomplished by a cyclicprocess involving separate zones for catalytic reaction, steamstripping, and catalyst regeneration. The hydrocarbon feedstock isblended with an appropriate amount of catalyst particles, and themixture so produced is then passed through a catalytic reactor, commonlycalled a riser, wherein a catalytic cracking reaction zone is maintainedsuch that at a temperature between about 800° and 1100° F. the feedstockis converted into gaseous, lower boiling hydrocarbons. After these lowerboiling hydrocarbons are separated from the catalyst in a suitableseparator, such as a cyclone separator, the catalyst, now deactivatedwith coke deposited upon its surfaces, is passed to a stripper. In thestripper, the deactivated catalyst is contacted with steam so as toconvert some of the coke to hydrocarbon product vapors, which are thencombined with the vapors received from the cyclone separator, and themixed vapors are then transferred to other facilities for furthertreatment. Meanwhile, catalyst particles are recovered from thestripper, and because only a small proportion of the coke is removed inthe stripper, the catalyst is introduced into a regenerator wherein, bycombustion in the presence of an oxygen-containing gas such as air, theremaining, larger proportion of coke is removed and the catalystreactivated. The cyclic process is then completed by blending thereactivated catalyst particles with the feedstock entering the riser ofthe FCC unit.

One recognized problem in the conventional FCC process resides in theincomplete combustion in the regenerator. Due to the relatively lowtemperature of combustion in the regenerator, usually between about 900°and about 1300° F., the flue gas contains carbon dioxide and carbonmonoxide in a ratio of 0.8:1 to about 10:1, CO₂ :CO, with the carbonmonoxide concentration often being as high as 15 mole percent. Such highconcentrations of carbon monoxide are a source of concern inasmuch ascarbon monoxide is a pollutant, and this concern has recently resultedin numerous methods to reduce the amount of carbon monoxide dischargedfrom FCC regenerators and the like. In general, these methods aim toreduce the polluting effects of carbon monoxide by incorporating intothe cracking catalyst particles metal components that are active forcatalyzing the reaction of CO with oxygen at the relatively lowtemperatures encountered in FCC regenerators. Alternatively, the metalCO oxidation promoter may be incorporated on particles havingsubstantially no catalytic cracking activity that circulate in the FCCunit with the catalyst particles. The metal promoters useful for suchpurposes include the Group VIII metals and rhenium, as disclosed in U.S.Pat. No. 4,072,600, chromium, as disclosed in U.S. Pat. No. 2,647,860,Group IB, IIB, VIB, VIIB, and VIII metals, as disclosed in U.S. Pat. No.3,364,136, and certain rare earth metals, such as cerium, as taught inNetherlands Pat. No. 7300884, and lanthanum, as taught in U.S. Pat. No.4,137,151.

The processes described in the foregoing prior art references usuallyentail substantial costs due to the expense involved in impregnatingselected metals onto catalyst particles. For example, if a certain rareearth element is desired as the CO oxidation promoter, substantial costsare incurred in extracting the selected rare earth element from an oreand separating it from the other metals also extracted from the ore. Inaddition, added costs are involved in modifying cracking catalysts so asto include the selected rare earth element thereon. Usually, theselected metal is incorporated upon the catalyst particles by animpregnation-calcination procedure which substantially increases thecost in manufacturing a cracking catalyst. Thus, the prior art approachto reducing CO emissions from FCC units is costly and one aim of the arthas been to reduce such costs and at the same time obtain significantreductions in CO emissions.

In addition to the problem of reducing CO emissions from FCC units,another major pollution problem is presented when the hydrocarbonfeedstock contains organic sulfur compounds. Ideally, the sulfurcompounds in a feedstock treated in an FCC unit are converted to H₂ S inthe catalytic reaction and stripping zones so that all the containedsulfur in the feedstock is recovered as H₂ S with the product vapors andlater separated therefrom by contact with an aqueous alkanolaminesolution. But in practice, it has been found that some sulfur componentsremain (or are converted to forms which remain) with the coke on thedeactivated catalyst recovered from the stripper. Hence, when the cokeis combusted in the regenerator, a flue gas containing SO_(x) compoundsis produced.

The flue gas, if untreated, is a source of pollution. Although about90-95% of the sulfur compounds entering an FCC unit with the feedstockare ultimately removed as H₂ S and other gaseous sulfur compounds, theremaining 5-10% left with the coke and converted to SO_(x) compounds inthe regenerator represents a significant environmental and engineeringproblem. For a typical FCC unit handling a feedstock containing about1.5 weight percent sulfur components (calculated as elemental sulfur)fed at a rate of about 50,000 barrels per day, the amount of SO_(x)compounds discharged from the regenerator in one day is between about3.0 and 10 tons (calculated as SO₂).

Because of the concern created by the discharge to the atmosphere ofSO_(x) compounds in such large quantities, various methods have beendevised to reduce SO_(x) emissions from FCC units to environmentallytolerable levels. Recently, attempts have been made to reduce suchSO_(x) emissions by recycling with the catalyst particles in the FCCunit a metal-containing component, commonly called a "sulfur getter,"that reacts in the regenerator with the gaseous SO_(x) compounds toyield a solid sulfur compound. The produced sulfur compound is thenreconverted to the active "sulfur gettering" form by passage through theriser and stripper wherein the solid sulfur compounds are decomposed torelease H₂ S. The release H₂ S is then recovered with the low-boilinghydrocarbons produced in the stripper and riser and then separated fromsaid low-boiling hydrocarbons, as stated before, by contact with analkanolamine solution.

One method illustrating the use of a "sulfur getter" is described inU.S. Pat. No. 3,835,031, wherein magnesium oxide is incorporated on thecatalyst for the purpose of scavenging SO_(x) compounds. In theregenerator, the magnesium oxide reacts with the SO_(x) compounds toproduce magnesium sulfate, thereby preventing the release of SO_(x)compounds from the regenerator. As the catalyst particles are recycledthrough the catalytic cracking and steam stripping zones maintained inthe riser and stripper, respectively, the magnesium sulfate is convertedback to magnesium oxide while the contained sulfur is released ashydrogen sulfide and collected with the low boiling hydrocarbonproducts. Thus, the catalyst particles, when recycled to the regeneratoragain, contain a magnesium compound (i.e., magnesium oxide) in an activeform for removing SO_(x).

Similar processes have been taught in U.S. Pat. Nos. 3,699,037,4,071,436, 4,137,151, 4,146,787, and 4,153,535. These referencesdisclose many metals for reducing the amount of SO₂ discharged from FCCregenerators. Usually, the metals are incorporated onto the catalystitself, but some references also disclose FCC processes whereinparticles separate from the catalyst are introduced into the FCC unitand recycled with the catalyst to control sulfur oxides emissions. U.S.Pat. No. 4,071,436, for example, teaches a process wherein particles ofreactive alumina are circulated with the catalyst particles. And U.S.Pat. No. 4,146,463 discloses thirteen specific metals plus the Group IIand rare earth metals for removing SO₂ produced in FCC regenerators, andthe metals so disclosed are taught as useful when impregnated on thecatalyst itself, incorporated on an insert substrate (i.e., inert forcracking hydrocarbons), or utilized as a powdered oxide.

One difficulty residing in the foregoing processes is that the "sulfurgetter" material must be prepared by processes involving substantialmanufacturing costs. An object of the present invention, therefore, isto improve upon the prior art processes by utilizing an abundant andinexpensive material, namely bastnaesite, as the "sulfur getter,"thereby substantially reducing the cost of removing SO₂ from FCCregenerators. It is yet another object of the invention to introducebastnaesite into the catalyst cracking cycle for the purpose ofsimultaneously lowering SO_(x) and CO emissions from the regenerators ofFCC units. It is yet another object of the invention to reduce SO_(x)and CO emissions from FCC regenerators and the like by introducingbastnaesite, either in a particulate form separate from the catalyst orin a form physically attached to the catalyst, into the FCC cycle forthe purpose of scavenging SO_(x) and/or catalyzing the conversion of COto CO₂ in the FCC regenerator. These and other objects will become moreapparent in view of the following description of the invention.

SUMMARY OF THE INVENTION

This invention is directed to preventing or reducing CO and/or SO_(x)emissions from catalytic cracking processes in which petroleumfeedstocks are refined into valuable hydrocarbon products. The inventioncomprises introducing particles of bastnaesite into the catalyticcracking cycle to react with sulfur oxides produced in the regenerationzone and simultaneous therewith to catalyze the conversion of CO to CO₂.The bastnaesite particles may be introduced into the FCC unit in amanner such that the bastnaesite particles are admixed with the crackingcatalyst particles but remain a separate entity therefrom, or thebastnaesite particles may be physically incorporated into the crackingparticles, as by making a minor change in the preparation of thecracking catalyst.

The invention is especially designed for lowering the carbon monoxideand sulfur oxides emissions from FCC units and other cyclical catalyticcracking processes wherein the catalyst particles are circulatedsuccessively through catalytic cracking, steam stripping, andregeneration zones. With respect to reducing sulfur oxides emissions,the bastnaesite particles are believed firstly to react with SO_(x)compounds, thereby reducing the amount of SO_(x) compounds dischargedwith the flue gas leaving the regenerator. Subsequently, the solidsulfur compounds are decomposed to produce H₂ S during passage throughthe catalytic cracking and steam stripping zones of the cracking cycle,thereby activating the bastnaesite particles once again for removingSO_(x) compounds in the regeneration zone. With respect to reducing COemissions, the bastnaesite particles in the regenerator have catalyticoxidation properties and are active for reacting CO with availableoxygen to produce CO₂.

All references herein to SO_(x) compounds are directed to one or moresulfur components selected from the group consisting of SO₂ and SO₃.

DETAILED DESCRIPTION OF THE INVENTION

In accordance with this invention, the fluidized catalytic cracking(FCC) process, or other cyclic catalytic cracking process in which ahydrocarbon feedstock is refined to produce low-boiling hydrocarbonproducts by passage through a catalytic cracking reaction zone, isimproved by introducing bastnaesite particles into the cyclic process toreduce the amount of SO_(x) and CO compounds emitted with the flue gasesdischarged from the regenerator. Bastnaesite is a rare earthfluorocarbonate mineral usually found in nature in contact with zincloads. As the raw mineral, bastnaesite contains about 65 to 80% byweight of assorted rare earth elements (calculated as the rare earthoxides), and at present is the primary industrial source for the lightrare earth elements. In particular, although containing significantproportions of praseodymium, neodymium, samarium, europium, andgadolinium, bastnaesite primarily contains lanthanum and cerium, usuallyin proportions exceeding 80% of the total rare earth content of themineral.

It will be understood herein that bastnaesite being a chemicallyreactive mineral undergoes chemical changes in the catalytic crackingunit. Similarly, if bastnaesite is utilized in the invention in apretreated form, such as in a steamed, leached, or calcined form, it mayhave a somewhat different composition than bastnaesite as found innature. For example, it has been found when natural bastnaesite iscalcined in air at a temperature around 700° C. that the mineralundergoes a chemical reaction such that some of the rare earthfluorocarbonates therein are converted to rare earth oxyfluorides. Also,natural bastnaesite may be leached with hydrochloric acid to separatestrontium and barium therefrom. Thus, it is within the scope of theinvention to use bastnaesite in modified forms, and for purposes herein,the term "bastnaesite" is meant to include not only bastnaesite as foundin nature (i.e., a natural bastnaesite) but also any material having adistribution of rare earth elements to total rare earth elementssubstantially similar to bastnaesite. A typical chemical analysis ofnatural bastnaesite reveals that the proportion of individual rare earthelements (calculated as the oxide) to the total rear earth elementcontent (calculated as the oxides) falls within the following ranges: 45to 55 wt. % CeO₂, 29 to 35 wt. % La₂ O₃, 11 to 15 wt. % Nd₂ O₃, 2.5 to5.5 wt. % Pr₂ O₃, 0.3 to 0.7 wt. % Sm₂ O₃, 0.1 to 0.3 wt. % Gd₂ O₃, 0.05to 0.15 wt. % Eu₂ O₃, and 0.05 to 0.35 wt. % of other rare earthelements, calculated as RE₂ O₃. For purposes herein, a material isconsidered to be bastnaesite when its proportions of individual rareearth elements (in elemental or combined forms) to total rare earthelements (in elemental or combined forms) are substantially within theforegoing ranges.

In accordance with this invention, bastnaesite particles are introducedinto a fluid catalytic cracking unit, usually by admixing thebastnaesite particles with the catalyst particles and then blending theresulting mixture into the unit at a convenient location. The amount ofbastnaesite so added will vary with the individual cracking unit andwith the amount of CO and SO_(x) desired to be removed from theregenerator flue gas. Usually, the bastnaesite particles are added at arate such that, of the total amount of catalyst particles andbastnaesite particles recirculating through the unit, 5.0 to 20% of suchparticles constitute bastnaesite.

The average size of the bastnaesite particles introduced into the FCCunit is most preferably the same as that of the catalyst particlesthemselves, i.e., about 20 to 80 microns in diameter. However, at thepresent time, bastnaesite is produced in abundance in a mixture ofparticle sizes ranging between about 1 and 65 microns. Accordingly, itis a preferred embodiment of the invention to introduce a mixture ofdifferently-sized bastnaesite particles ranging between about 1 andabout 65 microns into an FCC unit for the purpose of reducing CO and/orSO_(x) emissions.

The process of the invention is directed to lowering the amount ofgaseous pollutants discharged from regenerators of FCC units and thelike treating liquid hydrocarbon feedstocks, especially those containingsulfur. Typical feedstocks converted to lower boiling hydrocarbons insuch units include sulfur-containing gas oils, residual fractions, oilcrudes, naphthas, and the like. The total concentration of sulfur inmost FCC feedstocks, whether the sulfur is present in elemental orcombined forms or both, is between about 0.1 and 3.0 percent by weight(as sulfur). Usually, almost all the contained sulfur in the hydrocarbonfeedstock is present as organic sulfur compounds rather than free sulfuror inorganic compounds thereof.

In the process of the invention, any suitable cracking catalyst known inthe art to have cracking activity at elevated temperatures, such asabove about 750° F., may be utilized, but the preferred catalysts arethe high-activity fluidizable cracking catalysts. Generally, fluidizablecracking catalysts are in particulate form and comprise an inorganic,porous refractory oxide, such as silica-alumina. Usually, the crackingcatalyst also comprises crystalline aluminosilicates, such as X and Ytype zeolites. Preferred catalysts, however, comprise the Y type zeolitein a matrix of a porous, inorganic refractory oxide, such assilica-alumina or "beneficiated" natural clays, i.e., clays from whichdeleterious metal components have been removed. The crystallinealuminosilicate zeolites utilized in cracking catalysts may be renderedsubstantially more active for cracking hydrocarbons by ion exchange, amethod well-known in the art by which the sodium and other alkali metalions in the aluminosilicate structure are exchanged for rare earthelement ions, ammonium ions, hydrogen ions, or combinations thereof.Such ion exchange methods usually reduce the sodium and other alkalimetal ion content of the zeolites to a very low proportion, usually lessthan about 4.0% by weight (calculated as the alkali metals). The mosttypical and preferred catalyst for use in the invention comprises acrystalline aluminosilicate zeolite dispersed in silica-alumina, withthe alumina proportion of the finished catalyst being between about 25and 60 percent by weight and the zeolite proportion being between about5 and 20 percent by weight.

In the riser, the circulating bastnaesite and catalyst particles aremixed with the incoming feedstock in a fluidized catalytic crackingreaction zone. Conditions in the riser are selected from thoseconventionally used to produce the required product from the feedstock.Typically, reaction temperatures and pressures are between about 750°and 1150° F. and 14 and 40 psig, respectively. Fluidizing velocity willusually be in the range of 20 to about 60 feet per second, and theresidence time of the catalyst-feedstock-bastnaesite blend within theriser is between about 2 and 60 seconds. The weight ratio of catalyst tofeedstock will usually vary in the 2:1 to 15:1 range, and, preferably,the riser itself comprises a reaction vessel in which the blend ofcatalyst particles, hydrocarbon feedstock, and bastnaesite is fedvertically and concurrently. Also preferably, the ratio of height toaverage diameter of the reaction vessel comprising the riser is at least20, and most preferably at least 35.

Under the above conventional fluid catalytic cracking conditions, andwith the blend of feedstock, bastnaesite, and catalyst particles movingcocurrently through the reaction zone, the feedstock is converted in theriser into valuable hydrocarbon products of lower average molecularweight and of lower average boiling point. Some of the feedstock,however, is converted to coke, which accumulates upon the surfaces ofthe catalyst particles and thereby deactivates such catalyst particlesfor further cracking of hydrocarbons into product hydrocarbons. Althoughmuch of the sulfur present in the original feedstock is largelyrecovered with the product hydrocarbon vapors in the form of H₂ S andsulfur-containing hydrocarbonaceous vapors, a significant proportion ofthe sulfur remains in various organic forms with the coke deposited onthe catalyst particles. Usually, the concentration of sulfur in combinedand elemental forms in the coke ranges between about 0.5 and 12.0percent by weight (as sulfur).

The materials withdrawn from the riser include product oil vapors,hydrogen sulfide, deactivated catalyst particles, and bastnaesiteparticles. In a suitable separation zone, such as a cyclone separator,the product hydrocarbon vapors and hydrogen sulfide are separated fromthe deactivated catalyst and bastnaesite particles and sent toconventional processing facilities for removing the hydrogen sulfidefrom the product vapors. The catalyst and bastnaesite particles,however, are delivered to a stripper where, in the presence of astripping gas such as nitrogen or steam, with steam being preferred, thecoke on the catalyst is partially converted to valuable hydrocarbonvapors, while some of the sulfur compounds within the coke are partiallyconverted to H₂ S. Conditions within the stripper are preferablymaintained so as to recover as much H₂ S-containing hydrocarbon productvapors as is economically possible. Usually, the temperature within thestripping vessel is held in the 850° to 1050° F. range while pressuresare suitably maintained at between about 25 and about 50 psig.

After being transferred to a suitable separator, such as a cycloneseparator, the stripped catalyst particles and the bastnaesite particlesare separated from a product gas containing hydrocarbon vapors and H₂ S.The stripped catalyst is then transferred to a regenerator wherein, bycontact at elevated temperatures in the 900° to 1400° F. range with afree oxygen-containing gas, such as air, passed countercurrently to thestripped catalyst, the coke not converted to product vapors in thestripper is combusted, thereby removing it from the catalyst particles.When the coke is removed from the catalyst particles such that saidparticles contain coke in a proportion less than about 0.5 catalystweight percent, preferably less than about 0.2 catalyst weight percent,the catalyst particles are restored to an acceptably active state andare recycled to the riser. (As calculated herein, catalyst weightpercent refers to the percentage proportion of a substance on thesurfaces of catalyst particles to the weight of the catalyst particlesthemselves, exclusive of any material thereon. Thus, for example, if 100lbs. of catalyst particles contained 1 lb. of coke on the surfacesthereof, the coke would be present in a proportion of 1 catalyst weightpercent.)

Most of the catalyst particles recovered from the regenerator arerecycled to the riser for use therein to crack hydrocarbons, but some iscontinuously removed from the FCC unit because, after many cycles ofoperation, the catalyst particles gradually lose activity. Thus, in atypical FCC unit, about 1 to 5 percent of the catalyst inventory isreplaced by fresh catalyst each day, and concomitantly therewith,bastnaesite particles are fed to the unit to replace those removed withthe catalyst particles and thus maintain the proportion of bastnaesiteparticles to bastnaesite plus catalyst particles in the unit at aspecified, desired level sufficient to reduce regenerator SO_(x) and/orCO emissions below the amount produced by a similarly operating unit butcirculating only cracking catalyst particles.

Normally, the amount of SO_(x) compounds discharged from a conventionalregenerator by the conversion of the sulfur in the combusted coke to SO₂and SO₃ is between 3 and 30 tons per day (calculated as SO₂) while theamount of CO discharged is usually between about 50 and 300 tons perday, depending upon the size of the FCC unit, the concentration ofsulfur within the coke, and the operating conditions of the regenerator.But due to the presence of the bastnaesite particles, the amount ofSO_(x) discharged on a mass per hour basis with the flue gases issubstantially reduced by the chemical reaction of the SO_(x) with thebastnaesite to produce solid sulfur compounds within the bastnaesiteparticles. Similarly, the amount of CO discharged with the flue gaseswhen bastnaesite is present in the FCC unit is substantially reduced,the bastnaesite acting as a catalyst for the conversion of CO to CO₂ inthe presence of free oxygen. The amount by which the CO and SO_(x)pollutants will be lowered for a given catalytic cracking unit willdepend upon such factors as the size of the unit, the amount ofbastnaesite employed, and the conditions of operation. In one embodimentof the invention described more fully hereinafter in the ComparativeExample, SO_(x) was reduced by more than 75% (from 700 ppmv to about 140ppmv) and CO from 1.30 vol.% to about 0.9 vol.% in comparison to thesame unit operating in essentially the same manner but without thepresence of bastnaesite particles among the recirculating catalystparticles.

One factor having an effect on the amount by which SO_(x) and COemissions are decreased is the nature of the bastnaesite itself. In themost highly preferred embodiment of the invention, natural bastnaesiteparticles rather than bastnaesite particles treated by steaming,leaching, calcining, or the like are introduced into the FCC cycle,preferably by introduction directly into the regenerator in admixturewith fresh catalyst particles. Natural bastnaesite has been found tohave a substantially higher activity for reducing SO_(x) and COemissions than is the case for bastnaesite particles subjected tosteaming prior to introduction into the FCC unit, and it is believedthat natural bastnaesite would also perform more effectively than othermodified or treated forms of bastnaesite. Accordingly, in the mosthighly preferred embodiment of the invention, untreated, naturalbastnaesite is fed to the FCC regenerator for the purpose of reducingSO_(x) and CO emissions.

An important advantage in the invention is that the bastnaesiteparticles, once they have removed SO_(x) compounds in the regenerator,are subsequently regenerated in the riser and/or stripper to form onceagain active for removing SO_(x) compounds from the gases produced inthe regenerator. In other words, the bastnaesite particles, as theycontinuously recycle through the riser, stripper, and regenerator,alternately remove SO_(x) compounds from the regenerator flue gases andsubsequently release them in the riser and stripper in the form of H₂ S,the H₂ S then being removed with the other gases produced in the riserand stripper. The bastnaesite particles thus undergo alternate changesin chemical form, involving oxidation reactions in the regenerator andreduction and/or hydrolysis reactions in either the riser or stripper orboth. In the regenerator, the bastnaesite particles are believed toreact with SO_(x) compounds to produce solid compounds containing bothsulfur and rare earth element atoms and thereby reduce the amount ofSO_(x) compounds discharged from the regenerator with the flue gas. Inthe riser, at least some of the solid compounds containing both rareearth element and sulfur atoms release H₂ S and are thereby converted toforms suitable for subsequently removing SO_(x) compounds in theregenerator. Reactions similar to those in the riser may also take placein the stripper, resulting in the release of the sulfur contained in thebastnaesite as H₂ S and the rejuvenation of the bastnaesite to a formmore active for removing SO_(x) compounds in the regenerator.

The following Comparative Example, which is provided for the purpose ofillustrating the improved performance obtainable in the invention andnot to limit the scope thereof, demonstrates the superior reductions ofCO and SO_(x) in regenerator flue gases obtained by introducingbastnaesite into an FCC unit.

COMPARATIVE EXAMPLE

In a first experiment, a sulfur-containing gas oil feedstock having thechemical and physical properties shown in Table I was fed to a cyclicalcatalytic cracking unit of pilot plant size at the rate of about 1300gm/hr. Circulating through the catalytic cracking reaction zone, thestripping zone (utilizing nitrogen as the stripping gas), and theregeneration zone of the unit were about 3800 gm. of commercial crackingcatalyst particles pretreated by steam to lower the activity thereof toa stabilized level. The cracking catalyst was HEZ-53 marketed by HoudryDivision of Air Products and Chemicals, Inc., and the rate at which thecatalyst particles were circulated through the unit was 180 gm/min.Fluidizing conditions were maintained in the catalytic cracking reactionzone, and the temperature and pressure utilized therein were about 965°F. and about 20 psig, respectively.

After steady state conditions had been achieved, the flue gas emittedfrom the regenerator was analyzed for SO_(x), CO, and CO₂, and samplesof the catalyst particles entering and leaving the regeneration vesselwere taken and analyzed by appropriate techniques to determine theamount of coke thereon. Based upon other experiments wherein the sulfurcontent of the coke deposited upon the catalyst particles utilized totreat the feedstock of Table I was found to be about the same as that ofthe feedstock itself, the sulfur content of the coke on the catalystparticles herein was assumed to be about 1.17 wt.%. The data obtainedfrom analyzing the flue gas for SO_(x), CO₂, and CO are shown in TableII. Also shown in Table II are data pertaining to the proportion of cokeon the spent catalyst (CSC) entering the regenerator, the proportion ofcoke on the regenerated catalyst particles (CRC) leaving theregenerator, and the calculated difference between the proportion ofcoke on the spent catalyst particles and that on the regeneratedcatalyst (ΔC).

A second experiment was performed in a manner similar to the firstexcept that (1) 15% by weight of the catalyst particles were replacedwith an equivalent weight of bastnaesite particles having an averagesize of 28.6 microns and (2) the feed rate of the feedstock was somewhatlowered to maintain the same catalyst to oil ratio as in the firstexperiment. Data obtained in the second experiment are tabulated inTable II, and as shown, the SO_(x) and CO emissions were slightlyreduced in comparison to the emissions produced in the first experiment.

Because it was believed that the relatively poor performance in thesecond experiment was due to the presence of too much coke (high CRC) onthe bastnaesite particles recovered from the regenerator and thattherefore the surfaces of the bastnaesite were not adequately exposed tothe gases produced in the regenerator, a third experiment was performedsimilar to the second except that the conditions of the regenerator wereslightly changed to add more air to support combustion and consume moreof the coke (lower the CRC) on the catalyst and bastnaesite particles.The data obtained from the third experiment are presented in Table II,and as shown, a remarkable improvement in SO_(x) and CO removal wasfound. Despite the fact that more coke was burned in the regenerator perpass during the third experiment than in the second experiment (therebyconsequently releasing more SO_(x) and CO_(x) compounds than in thesecond experiment), the proportion of SO_(x) compounds and theproportion of CO in the flue gas was much lower in the third experimentthan in the second experiment.

In view of the data shown in Table II, it is apparent when theproportion of coke on the regenerated catalyst and bastnaesite particlesis reduced to low levels that the bastnaesite particles become moreefficient for scavenging SO_(x) and also more efficient for catalyzingthe oxidation of CO. For different catalysts, of course, the lowproportion of coke required to provide such high reductions in SO_(x)and CO will vary but normally will be less than about 0.2 catalystweight percent. Accordingly, it is a specific embodiment of theinvention to utilize bastnaesite particles in a cyclic cataltyiccracking unit and to so operate the regenerator associated therewiththat the proportion of coke on the catalyst particles leaving theregenerator (CRC) is less than about 0.2 catalyst weight percent,preferably less than about 0.15 catalyst weight percent.

                  TABLE I                                                         ______________________________________                                        FEEDSTOCK ANALYSIS                                                                              ASTM Distilla-                                                                tion D1160                                                                    Volumetric Cut                                                                          °F.                                        ______________________________________                                        Gravity, °API                                                                          23.1                                                          Sulfur, Wt. %   1.17    1/5         316/476                                   Conradsen Carbon, Wt. %                                                                       0.12    10/20       541/641                                   Ramsbottom Carbon, Wt. %                                                                      0.17    30/40       693/738                                   Nitrogen, Wt. % 0.300   50/60       774/806                                   Arsenic, ppmw   <0.5    70/80       838/869                                   Aniline Point, °F., D611                                                               151     90/95       911/947                                   Bromine No. Elect.                                                                            12.3    Maximum     1002                                                              Recovery,   98.9                                                              Vol. %                                                ______________________________________                                    

                  TABLE II                                                        ______________________________________                                                    First                                                                         Experi-                                                                              Second     Third                                                       ment   Experiment Experiment.sup.1                                ______________________________________                                        Composition of                                                                              100%     15%        15%                                         Circulating Particles                                                                       HEZ-53   Bastnaesite                                                                              Bastnaesite                                               Catalyst and 85%    and 85%                                                            HEZ-53     HEZ-53                                                             Catalyst   Catalyst                                    Flue Gas Composition                                                          SO.sub.x, ppmv                                                                              700      640        140                                         CO, vol. %    1.30     1.25       0.9                                         CO.sub.2, vol. %                                                                            7.5      8.5        8.6                                         CO.sub.2 :CO  5.8      6.8        9.5                                         Coke on Spent Catalyst                                                        (CSC), Catalyst Wt. %                                                                       0.93     0.79       0.73                                        Coke on Regenerated                                                           Catalyst (CRC),                                                               Catalyst Wt. %                                                                              0.25     0.25       0.10                                        ΔC (CSC - CRC)                                                                        0.68     0.54       0.63                                        ______________________________________                                         .sup.1 When the third experiment was continued at a later point in time,      initial SO.sub.x concentration was 115 ppmv, the CO concentration was 1.0     vol. %, and the CO.sub.2 :CO ratio was 9.4.                              

In an alternative embodiment of the invention, the bastnaesite particlesare physically embodied into the cracking catalyst particles. Thus,where the typical cracking catalyst particles comprise a crystallinealuminosilicate zeolite dispersed in an inorganic refractory oxidematrix, the catalyst of the invention will further comprise bastnaesiteparticles dispersed in the refractory oxide matrix. Illustrative of thisembodiment of the invention is a cracking catalyst comprising particlesof bastnaesite and particles of a rare earth stabilized Y zeolitedispersed in larger particles of silica-alumina.

In non-preferred embodiments of the invention, the catalyst utilized inthe FCC unit is modified so as to comprise bastnaesite particlesdispersed in a refractory oxide matrix, with no crystallinealuminosilicate zeolites also dispersed therein. Such catalystsparticles will usually have substantially lower cracking activity andlower selectivity than is the case for catalysts containing crystallinealuminosilicates.

The method by which the bastnaesite particles are dispersed in orotherwise intimately bound to the inorganic refractory oxide is notcritical and may easily be accomplished by making minor changes in themethod of preparing conventional cracking catalyst particles. Forexample, in commercial practice wherein a catalyst comprising acrystalline aluminosilicate zeolite dispersed in an inorganic refractoryoxide matrix is desired, the preparation procedure usually involvessubjecting a slurry of zeolite particles, inorganic refractory oxideparticles, and an appropriate binder material in an aqueous medium tospray drying. The slurry usually comprises about 18% solids, and thespray drying procedure is designed to produce a catalyst having adesired zeolite to refractory oxide ratio and, more importantly, acatalyst of desired particulate size. In accordance with the invention,however, the foregoing slurry is modified so that, upon spray drying,the bastnaesite particles are physically incorporated into theparticulate aggregates also containing the refractory oxide and thezeolite particles. Usually, sufficient of the bastnaesite particles areincluded in the slurry such that the resulting catalyst contains betweenabout 1.0 to 20% by weight of bastnaesite, with the remainder comprisingone or more porous, inorganic refractory oxides and, preferably, furthercomprising one or more crystalline aluminosilicates having activity forcracking hydrocarbons at temperatures of about 750° to 1150° F.Preferred catalysts of the invention comprise 5.0 to 20% by weightbastnaesite, 5 to 20% by weight crystalline aluminosilicate zeolite, andthe balance a porous, inorganic refractory oxide.

Bastnaesite-containing cracking catalysts made by the foregoingprocedure or by other methods readily apparent to those skilled in theart are utilized in an FCC unit under appropriate conditions to effectthe intended hydrocarbon conversions in the catalytic cracking reactionzone. When the cracking catalyst particles become coked and are passedto the regeneration zone, the presence of the bastnaesite in thecracking catalyst reduces CO and SO_(x) emissions, with the latterespecially being reduced when the coke content of the catalyst particlesrecovered from the regeneration step is less than about 0.2 catalystweight percent.

Although the invention has been described in conjunction with preferredand alternative embodiments thereof, it is evident that manyalternatives, modifications, and variations of the invention will beapparent to those skilled in the art in light of the foregoingdescription. Accordingly, it is intended to embrace within the inventionall such alternatives, modifications, and variations that fall withinthe spirit and scope of the appended claims.

We claim:
 1. In a process for regenerating cracking catalyst particleshaving sulfur-containing coke on the surfaces thereof by combusting saidcoke in the presence of oxygen and at elevated temperatures so as toremove sufficient coke from the surfaces of said catalyst particles soas to reactivate said catalyst particles for cracking hydrocarbons whileproducing a flue gas containing one or more pollutant gases selectedfrom the group consisting of SO_(x) and CO, the improvement for reducingthe amount of at least one of said pollutant gases carried with saidflue gas comprising:(1) introducing into a regeneration zone a feedadmixture of catalyst particles deactivated with coke and bastnaesiteparticles containing natural bastnaesite or a treated naturalbastnaesite containing a rare earth fluorocarbonate or rare earthoxyfluoride after use of said admixture in a catalytic cracking reactionzone wherein hydrocarbons are cracked to produce product hydrocarbons oflower average molecular weight and boiling point; (2) combusting, insaid regeneration zone, a substantial proportion of the coke on saidcatalyst particles admixed with said bastnaesite particles; and (3)withdrawing a product admixture of bastnaesite particles and regeneratedcracking catalyst particles from said regeneration zone, said productadmixture being more active for cracking hydrocarbons than said feedadmixture.
 2. A process as defined in claim 1 wherein the temperature insaid regeneration zone is between about 900° and 1400° F.
 3. A processas defined in claim 1 wherein (1) said catalyst particles comprise acrystalline aluminosilicate zeolite having activity for crackinghydrocarbons at a temperature above about 750° F. and (2) saidbastnaesite is in the form of particles having an average diameterbetween about 20 to 80 microns.
 4. A process as defined in claim 1wherein said bastnaesite and catalyst particles withdrawn from saidregeneration zone contain, on the average, less than about 0.2 catalystweight percent of coke.
 5. A process as defined in claim 1, 2, 3, or 4wherein said bastnaesite particles are physically embodied into thecatalyst particles.
 6. A process as defined in claim 5 wherein saidbastnaesite particles comprise about 1.0 to 20% by weight of both thefeed and product admixture of catalyst and bastnaesite.
 7. A process asdefined in claim 5 wherein said catalyst particles comprise acrystalline aluminosilicate zeolite containing rare earth ions exchangedthereinto, said zeolite being dispersed in a matrix of an inorganicrefractory oxide.
 8. In a process for regenerating cracking catalystparticles having sulfur-containing coke on the surfaces thereof bycombusting said coke in the presence of oxygen and at elevatedtemperatures so as to remove sufficient coke from the surfaces of saidcatalyst particles so as to reactivate said catalyst particles forcracking hydrocarbons while producing a flue gas containing one or moreSO_(x) compounds, the improvement for reducing the amount of said SO_(x)compounds carried with said flue gas comprising:(1) introducing into aregeneration zone a feed admixture of catalyst particles deactivatedwith coke and particles containing natural bastnaesite after use of saidadmixture in a catalytic cracking reaction zone wherein hydrocarbons arecracked to produce product hydrocarbons of lower average molecularweight and boiling point; (2) combusting, in said regeneration zone, asubstantial proportion of the coke on said catalyst particles admixedwith said particles of natural bastnaesite; and (3) withdrawing aproduct admixture of bastnaesite particles and regenerated crackingcatalyst particles, said product admixture being more active forcracking hydrocarbons than said feed admixture.
 9. In a process forregenerating cracking catalyst particles having coke on the surfacesthereof by combusting said coke in the presence of oxygen and atelevated temperatures so as to remove sufficient coke from the surfacesof said catalyst particles so as to reactivate said catalyst particlesfor cracking hydrocarbons while producing a flue gas containing CO, theimprovement for reducing the amount of CO carried with said flue gascomprising:(1) introducing into a regeneration zone a feed admixture ofcatalyst particles deactivated with coke and particles containingnatural bastnaesite after use of said admixture in a catalytic crackingreaction zone wherein hydrocarbons are cracked to produce producthydrocarbons of lower average molecular weight and boiling point; (2)combusting, in said regeneration zone, a substantial proportion of thecoke on said catalyst particles admixed with said particles of naturalbastnaesite; and (3) withdrawing a product admixture of bastnaesiteparticles and regenerated cracking catalyst particles from saidregeneration zone, said product admixture being more active for crackinghydrocarbons than said feed admixture.
 10. In a process for regeneratingcracking catalyst particles having sulfur-containing coke on thesurfaces thereof by combusting said coke in the presence of oxygen andat elevated temperatures so as to remove sufficient coke from thesurfaces of said catalyst particles so as to reactivate said catalystparticles for cracking hydrocarbons while producing a flue gascontaining SO_(x) and CO compounds, the improvement for reducing theamount of both SO_(x) and CO carried with said flue gas comprising:(1)introducing into a regeneration zone a feed admixture of catalystparticles deactivated with coke and particles containing naturalbastnaesite after use of said admixture in a catalytic cracking reactionzone wherein hydrocarbons are cracked to produce product hydrocarbons oflower average molecular weight and boiling point; (2) combusting, insaid regeneration zone, a substantial proportion of the coke on saidcatalyst particles admixed with said particles of natural bastnaesite;and (3) withdrawing a product admixture of bastnaesite particles andregenerated cracking catalyst particles from said regeneration zone,said product admixture being more active for cracking hydrocarbons thansaid feed admixture.
 11. A process as defined in claim 8, 9, or 10wherein said particles containing natural bastnaesite are physicallyembodied into the catalyst particles.
 12. A process as defined in claim11 wherein the catalyst particles withdrawn from said regeneration zonecontain, on the average, less than 0.15 catalyst weight percent of coke.13. A process as defined in claim 8, 9 or 10 wherein said bastnaesiteand catalyst particles withdrawn from said regeneration zone contain, onthe average, less than about 0.2 catalyst weight percent of coke.
 14. Aprocess as defined in claim 13 wherein said particles containing naturalbastnaesite are physically embodied into the catalyst particles.
 15. Aprocess as defined in claim 13 wherein the temperature in saidregeneration zone is between about 900° and 1400° F.
 16. A process asdefined in claim 15 wherein said catalyst particles comprise acrystalline aluminosilicate zeolite containing rare earth element ionsexchanged thereinto, said zeolite being dispersed in a matrix of aninorganic refractory oxide.
 17. A process as defined in claim 1, 8, 9 or10 wherein said catalyst particles comprise a crystallinealuminosilicate zeolite containing rare earth element ions exchangedthereinto, said zeolite being dispersed in a matrix of an inorganicrefractory oxide.